o:1919 Uticaj tehnike nagrizanja, svetlosno-polimerizujućeg režima i vrste kompozita na jačinu adhezivne veze za dentin primenom univerzalnog adhezivnog sistema The influence of etching mode, light curing mode and composite resin type on bond strength to dentin using universal adhesive system : doctoral dissertation sr Strong adhesive bond between the dentin and composite is mandatory for long-lasting composite restorations. However, establishing an optimal bond between two completely different substrates is extremely complex and depends on many different factors.This study aimed to examine and compare the influence of different etching modes, light-curing regimens and composite resin types on the immediate shear bond strength (SBS) to dentin using universal adhesive system.A total of 120 samples, consisting of flat dentin plates and cylindrical composite build-ups bonded by universal adhesive (3M Scotchbond Universal Adhesive), were formed to achieve the goal of this study. By combining different etching modes (total-etch / self-etch), composite resin types (conventional / bulkfill) and light-curing regimens (standard / modified), a total of 8 experimental groups were formed (n=15). Shear bond strength test was performed in a universal testing machine and failure force was recorded. Failure sites were examined via scanning electron microscopy.Out of three variables considered, Multivariate ANOVA showed significant interaction was found for variables composite resin type (p<0,001) and etching mode (p=0,001), while the influence of light-curing mode was insignificant (p=0,083). Significantly higher SBS was obtained when bulkfill composite was used compared to the conventional one (p<0,001), as well as total-etch mode compared to self-etch mode (p=0,005). The SBS differs significantly depending on the failure mode. Mixed failure mode was predominant in all sample groups. Adhesive failure resulted in lowest SBS (18,69±2,36 MPa), while cohesive failure in dentin resulted in highest SBS (31,67±4,64 MPa).Proper selection of dental restorative material and etching mode are of crucial importance for the formation of a strong adhesive bond and longevity of the composite filling. The strongest adhesive bond is achieved when total-etch mode and bulkfill composites are used, so they should be preferred whenever possible in the given clinical conditions. The use of modified light-curing regimens does notcontribute to higher bond strength and requires further improvement and standardization. Beleška o autoru: list 111,Bibliografija: listovi 96-110. Datum odbrane: 05.06.2023. Restorative Dentistry and Endodontics 91552100 119312649 91552101 8627 2023-09-18T08:46:29.053Z 45 no 46 Milan, 1989- Miljković 102251529 2023 63 mentor Stefan, 1978- Dačić 1975399 2023 63 predsednik komisije Aleksandar Mitić 2023 63 član komisije Mirjana Bošković 2023 63 član komisije Jelena Popović 2023 63 član komisije Dušan Petković 2023 114 listova 7920313 http://phaidrani.ni.ac.rs/o:1919 no yes 12 2023-09-18T08:46:29.320Z 70 jačina adhezivne veze, tehnika nagrizanja, svetlosna polimerizacija, kompozitne smole, univerzalni adhezivi, fraktografska analiza shear bond strength, etching mode, light curing, composite resin, universal adhesive, fractographic analysis 616.314-74:615.46]:66.095.26.085(043.3) B 730 1738 18A05 18A0529 2023